Effect of Relining Curing Methods on Some Properties of Acrylic Resin Denture Base (Part II)

Nadira A Hatim; Aliaa W AL-Omari

Al-Rafidain Dental Journal, Volume 13, Issue 2, Pages 211-220
DOI: 10.33899/rden.2013.84775

Aims: To investigate the effect of relining by using two curing methods (water bath, or microwave) on some properties ( surface hardness, color property, residual monomer, and porosity) of relined acrylic resin denture base. Materials and methods: The study was done by preparing 320 samples, divided into two parts, the first part involved studying surface hardness, color property, residual monomer, and porosity of samples representing a denture base cured by water bath curing method, and the samples of second part cured by microwave curing method, then the effect of relining by the two curing methods (water bath, and microwave) were evaluated. Samples with dimensions of 30×15×3 ± 0.03mm for the indentation hardness test, 45×10×2.5mm for the color property test, 20×20×3mm for residual monomer test were prepared in this study. Analysis of variance (ANOVA) and Duncan's multiple range tests were used for statistical analysis. Results: surface hardness of denture base cured by microwave was significantly higher (at P=0.05) than denture base cured by water bath, all the relined samples has sig-nificant higher absorbance, and showed that the elusion of monomer was higher at the 1st day. Conclu-sions: Surface hardness, color property and residual monomer of the acrylic resin denture base were affected by relining. Microwave curing method gave better mechanical, and physical properties of the relined acrylic resin denture base, the amount of residual monomer was less in the microwave curing method. Both curing methods gave samples free from porosities.

The Effect of Surface Treatment on the Transverse and Tensile Bonding Strength of Relined Acrylic Resin Denture Base (Part I)

Nadira A Hatim; Aliaa W AL-Omari

Al-Rafidain Dental Journal, Volume 13, Issue 2, Pages 202-210
DOI: 10.33899/rden.2013.84691

Aims: To investigate the effect of the thickness of relining material, curing method (water bath or mi-crowave), and the surface treatment by methyl methacrylate on transverse and tensile strength of re-lined acrylic resin denture base. Materials and methods: A pilot study was done by preparing 65 sam-ples to evaluate the effect of the thickness of relining material in relation to denture base on the trans-verse strength of acrylic resin denture base, and to study the effect of surface treatment by methyl methacrylate on the transverse strength of acrylic resin denture base. The main study was done by pre-paring 320 samples and divided into two parts to study the mechanical properties of samples represent-ing a denture base cured by water bath and other group cured by microwave curing technique, and then the effect of relining by the two curing methods and the effect of surface treatment were evaluated. Analysis of variance (ANOVA) and Duncan's multiple range tests were used for statistical analysis. Results: of this study showed that the different thickness of relining material in relation to denture base had no significant difference on the transverse strength of the relined denture base. The transverse strength and tensile bonding strength of the relined samples were significantly improved (P=0.05) by monomer surface treatment for 180 seconds. Conclusions: Transverse and tensile strength of the acryl-ic resin denture base were affected by relining. Microwave curing method gave better mechanical properties of the relined acrylic resin denture base.